Rashid Metals is a reputable manufacturer and supplier of M2 Steel Bars and Rods, proudly based in Muscat, Oman. They specialize in delivering top-notch tool steel products to a variety of industrial sectors. Renowned for their precision and consistent quality, Rashid Metals adheres to international standards, ensuring that their M2 steel products are perfectly suited for high-performance cutting and forming tasks. With cutting-edge processing capabilities and rigorous quality control, the company caters to both local and international clients. Rashid Metals is committed to providing a reliable supply, precise specifications, and technical support, making them a trusted source for M2 Steel Bars and Rods in demanding manufacturing settings.
M2 Steel Bars and Rods are crafted from high-speed tool steel, enriched with elements like tungsten, molybdenum, chromium, vanadium, and carbon. This thoughtfully balanced mix results in outstanding mechanical properties, including exceptional hardness, impressive wear resistance, and robust hot hardness. M2 steel retains its cutting efficiency even at high temperatures and boasts good toughness and compressive strength. Its fine carbide structure contributes to its durability, abrasion resistance, and performance in high-speed and high-load conditions.
| Specification | Details |
|---|---|
| Standard | ASTM A600, ASME SA600 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Form | Round |
| Diameter | 2mm to 100mm (depending on grades) |
| Length | 100 mm to 10,000 mm |
| Surface Condition | Black, Grinded, Turned Bright, Machined Proof |
| Maximum | Typical | ||||||
|---|---|---|---|---|---|---|---|
| Carbon | Chromium | Tungsten | Molybdenum | Vanadium | Cobalt | Annealed | Tempered |
| C | Cr | W | Mo | V | Co | Hb | HrC |
| 0.85 | 4.15 | 6.15 | 5.1 | 1.95 | – | 255 | 64 |
| Tensile strength | 1000-1400 MPa |
|---|---|
| Yield Strength | 3250 MPa |
| Abrasion (loss as-hardened; ASTM G65) | 25.8 mm3 |
| Impact Toughness | 67 J/cm2 |
| Hardness | 262 HRC |
| Modulus of elasticity | 207 GPa |
| Country | USA | German | Japan |
|---|---|---|---|
| Standard | ASTM A600 | DIN EN ISO 4957 | JIS G4403 |
| Grades | M2 | 1.3343 | SKH51 |
Yes, M2 steel can be welded, but it requires preheating and post-weld heat treatment to prevent cracking and ensure good weld strength due to its high hardness and wear resistance.
M2 steel rods are available in various sizes, typically ranging from 1/16" to 3" in diameter. Common finishes include bright, polished, and cold-drawn for enhanced surface quality and performance.
M2 steel bars are typically sized by diameter and length, with standard diameters ranging from 6 mm to 100 mm. Lengths usually vary from 3 meters to 6 meters.
In the manufacturing world, M2 Steel Bars and Rods are essential for creating high-performance cutting and forming tools. Common applications include drills, taps, milling cutters, reamers, broaches, saw blades, punches, and dies. They also find use in cold work tooling, gear cutting tools, and industrial knives. Thanks to their remarkable wear resistance, heat resistance, and strength, M2 steel products guarantee longer tool life, enhanced productivity, and dependable performance in high-speed machining and precision engineering tasks.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Rashid Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Muscat, OMAN