Rashid Metals is a trusted manufacturer and supplier located in Muscat, OMAN, providing a wide array of stainless steel products, including the notable Stainless Steel 1.4122 Bars. The company has built a solid reputation for its unwavering dedication to quality, precision in manufacturing, and strict adherence to international standards. Catering to various industries like engineering, automotive, tooling, and industrial machinery, Rashid Metals delivers materials that boast high strength, wear resistance, and reliable performance. With cutting-edge production capabilities, a team of skilled professionals, and rigorous quality control measures, the company guarantees that its Stainless Steel 1.4122 Bars meet the toughest technical specifications and application needs.
Stainless Steel 1.4122 Bars are martensitic stainless steels that contain about 15–17% chromium and a higher carbon content, usually around 0.45–0.55%. This unique composition allows the material to be effectively hardened through heat treatment. In terms of mechanical properties, 1.4122 Bars provide impressive tensile and yield strength, outstanding hardness, and excellent wear resistance. They also exhibit good fatigue strength and dimensional stability. While their corrosion resistance is moderate compared to austenitic grades, it is sufficient for mildly corrosive and industrial settings.
Length : 1 To 6 Meters, Custom Cut Length
Round bar : Diameter: 3mm~ 800mm
Angle bar : Size: 3mm* 20mm* 20mm~ 12mm* 100mm* 100mm
Square bar : Size: 4mm* 4mm ~100mm* 100mm
Flat bar : Thickness: 2mm ~ 100mm / Width: 10mm ~ 500mm
Hex bar : Size: 2mm ~ 100mm
Form : Round, Square, Hex(A/F), Rectangle, Billet, Ingot, Forging Etc
Surface Finishing : Pickled, Black, Bright, Polishing, Blasting, etc
Test Reports : SGS, BV, API, BSI, GHC.
Packing : Each steel bar has the singal, and several will be bundled by weaving bag or as per requirement.
Specials : Sizes and Specifications other than above can be manufactured on request
| Grade | C | Si | Mn | P | S | Cr | Mo | N | Others |
| SS 1.4122 | 0.33-0.45 | max 1.00 | max 1.5 | max 0.040 | max 0.015 | 15.5-17.5 | 0.80-1.30 | max 1.00 | – |
| Yield Rp0.2 (MPa) | Tensile Rm (MPa) | Impact KV/Ku (J) | Elongation A (%) | Reduction in cross section on fracture Z (%) | As-Heat-Treated Condition | Brinell hardness (HBW) |
| 869 (≥) | 926 (≥) | 41 | 44 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 444 |
| EN | DIN | AFNOR |
| 1.4122 | 1.4122 – X 39 Cr Mo 17 1 | Z 38 CD 16-01 |
Yes, Stainless Steel 1.4122 bars can be recycled after use. Stainless steel is highly recyclable, retaining its properties and reducing environmental impact, making it a sustainable material for reuse.
Yes, Stainless Steel 1.4122 bars can be welded. It is weldable using standard methods like TIG or MIG welding, though pre-heating and post-weld heat treatment may be required for optimal results.
Yes, Stainless Steel 1.4122 bars can be heat treated. It can be hardened through quenching and tempering processes, improving strength and wear resistance while maintaining its corrosion resistance properties.
These Stainless Steel 1.4122 Bars find extensive use in applications that demand high strength, hardness, and wear resistance. Common applications include shafts, fasteners, machine components, tooling parts, and precision-engineered components. They are frequently utilized in the automotive, mechanical, and industrial manufacturing sectors for parts that endure high stress and repeated loading. Additional uses encompass valve components, pump parts, bearings, and structural elements where durability, reliability, and a long service life are crucial.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Rashid Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Muscat, OMAN
Copyright 2024 Rashid Metals. All rights reserved