Rashid Metals, a reputable manufacturer and supplier located in Muscat, Oman, has built a solid reputation for providing top-notch Stainless Steel 416 Bars and Rods across various industries. With a keen emphasis on precision, durability, and customer satisfaction, the company guarantees that each product adheres to international standards. By employing cutting-edge production techniques, Rashid Metals crafts Stainless Steel 416 Bars and Rods that are known for their reliability and consistent performance. Catering to sectors like automotive, construction, machinery, and general engineering, the company is celebrated for its timely deliveries, technical know-how, and unwavering commitment to excellence in the stainless-steel industry.
Stainless Steel 416 Bars and Rods are made up of chromium, carbon, manganese, sulfur, and trace elements such as silicon and phosphorus. The increased sulfur content significantly boosts machinability, making SS 416 one of the most workable martensitic stainless steels available. These bars provide moderate corrosion resistance, along with good tensile and yield strength, and they become even harder after heat treatment. Their mechanical properties include impressive wear resistance and high durability, especially when hardened, ensuring they perform reliably in demanding applications.
Specification : ASTM A276, A479 / ASME SA276, SA479
Standard : EN, DIN, JIS, ASTM, BS, ASME, AISI
Round Bars : Outside Diameter in the range of 4mm to 500mm
Bright Bars : Outside Diameter in the range of 4mm to 100mm
Hex Bars : 18mm – 57mm (11/16″ to 2-3/4″)
Square Bars : 18mm – 47mm (11/16″ to 1-3/4″)
Finish : Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish
Length : 1 to 6 Meters, Custom Cut Lengths
Form : Round, Square, Hex (A/F), Rectangle Etc.
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
| SS 416 | 0.15 max | 1.25 max | 1.0 max | 0.06 max | 0.15 min | 14.00 – 12.00 | 0.6 | – | – |
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 8.0 g/cm3 | 1454 °C (2650 °F) | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 | 35 % |
| STANDARD | WERKSTOFF NR. | UNS | JIS | EN | BS |
| SS 416 | 1.4005 | S41600 | SUS 416 | X12CrS13 | 416S21 |
Stainless Steel 416 is a martensitic stainless steel with a higher level of sulfur and carbon content, which enhances its machinability compared to other stainless steels. This alloy offers improved strength and hardness while still maintaining a good level of corrosion resistance, making it suitable for precision machining.
Yes, Stainless Steel 416 can be heat-treated to increase its hardness. It can be hardened through a quenching and tempering process, which improves its strength, making it ideal for applications that require high wear resistance.
Thanks to their outstanding machinability and strength, Stainless Steel 416 Bars and Rods are widely used. They are perfect for creating gears, shafts, valves, pump components, and fasteners that require precision and reliability. In the automotive and mechanical engineering fields, they are often chosen for manufacturing studs, axles, and motor parts. Additionally, these rods find applications in industrial equipment, food processing machinery, and general-purpose tools. Their wear resistance and ability to endure moderately corrosive environments make them ideal for applications that demand long-lasting and dependable metal components.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Rashid Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Muscat, OMAN