Rashid Metals in Muscat, Oman proudly delivers Tool and Die Steel H13 Bars that stand as a symbol of endurance, precision and true industrial strength. H13 is a steel trusted globally for its ability to survive extreme heat and brutal working conditions, and Rashid Metals ensures every bar meets the highest expectations. These bars are crafted for industries where tools strike, press and shape metal under intense temperatures, yet must stay stable and reliable. With honest craftsmanship and consistent quality, H13 Bars help manufacturers build molds, dies and components that perform powerfully without losing shape or strength.
Tool and Die Steel H13 Bars contain a strong blend of chromium, molybdenum and vanadium, giving the steel exceptional hardenability and high temperature strength. This alloy maintains toughness even under thermal stress and resists cracking, softening and wear. H13 Bars show excellent compressive strength, stable hardness and great thermal shock resistance. Their ability to keep strength at elevated temperatures makes them a top choice for hot working tools. The steel also provides reliable machinability and dimensional stability after heat treatment, supporting precise industrial applications.
| ASTM A681 | C | Mn | P | S | Si | Cr | V | Mo | ||||||
| H13 | 0.32 | 0.45 | 0.2 | 0.6 | 0.03 | 0.03 | 0.8 | 1.25 | 4.75 | 5.5 | 0.8 | 1.2 | 1.1 | 1.75 |
| DIN ISO 4957 | C | Mn | P | S | Si | Cr | V | Mo | ||||||
| 1.2344 /X40CrMoV5-1 | 0.35 | 0.42 | 0.25 | 0.5 | 0.03 | 0.02 | 0.8 | 1.2 | 4.8 | 5.5 | 0.85 | 1.15 | 1.1 | 1.5 |
| JIS G4404 | C | Mn | P | S | Si | Cr | V | Mo | ||||||
| SKD61 | 0.35 | 0.42 | 0.25 | 0.5 | 0.03 | 0.02 | 0.8 | 1.2 | 4.8 | 5.5 | 0.8 | 1.15 | 1.0 | 1.5 |
| Properties | Metric | Imperial |
| Tensile strength, ultimate (@20°C/68°F, varies with heat treatment) | 1200 – 1590 MPa | 174000 – 231000 psi |
| Tensile strength, yield (@20°C/68°F, varies with heat treatment) | 1000 – 1380 MPa | 145000 – 200000 psi |
| Reduction of area (@20°C/68°F) | 50.00% | 50.00% |
| Modulus of elasticity (@20°C/68°F) | 215 GPa | 31200 ksi |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Country | USA | German | Japan |
| Standard | ASTM A681 | DIN EN ISO 4957 | JIS G4404 |
| Grades | H13 | 1.2344/X40CrMoV5-1 | SKD61 |
| Properties | Conditions | ||
|---|---|---|---|
| T (ºC) | Treatment | ||
| Thermal expansion | 10.4 x 10-6/ºC | 20-100 | – |
| Thermal conductivity | 28.6 W/mK | 215 | – |
When choosing Tool and Die Steel H13 bars, consider factors such as hardness, heat resistance, wear resistance, toughness, machinability, and the specific requirements of the application, including temperature and load conditions.
Tool and Die Steel H13 bars offer limited corrosion resistance due to their high alloy content, but they can still be susceptible to rusting in harsh environments. To improve corrosion resistance, they may require additional surface treatments like coating or regular maintenance to prevent degradation.
Tool and Die Steel H13 Bars are widely used in industries that push tools to extreme temperatures and harsh conditions. They are essential for hot forging dies, extrusion dies, die casting tools and heavy duty molds that must survive intense heat cycles. Manufacturing plants use H13 Bars for punches, shear tools, mandrels and cores that handle repeated impact. The automotive and aerospace sectors rely on them for parts that require thermal stability and long term durability. Thanks to their toughness and resistance to heat fatigue, H13 Bars remain a trusted material for high performance, high pressure tooling.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Rashid Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Muscat, OMAN
Copyright 2024 Rashid Metals. All rights reserved